Mediloy S-Co, Cobalt-Based Alloy for Dental Restorations

Mediloy® S-Co is a premium cobalt-chromium powder alloy specifically designed for the Selective Laser Melting (SLM) process, ensuring precision and strength in dental restorations. With its tried-and-tested composition of cobalt, chrome, wolfram, and molybdenum, this alloy is engineered for high stability, biocompatibility, and consistent quality in various dental applications.

Key Benefits for Dental Technicians:

• Proven Composition: The alloy is formulated with cobalt, chrome, wolfram, and molybdenum, offering reliable performance in dental restorations.
• Biocompatible and Safe: Mediloy® S-Co is free from nickel, cadmium, and beryllium, ensuring patient safety and preventing allergic reactions while maintaining excellent corrosion resistance.
• High Stability and Strength: With exceptional proof strength and ultimate tensile strength, this alloy guarantees highly stable constructions, even for long-span bridges and complex frameworks.
• Reliable System Parameters: Consistent system performance is achieved through the high-quality composition, ensuring predictable outcomes in every production cycle.
• Patent Protection: Using Mediloy® S-Co powder allows for the application of BEGO patents related to the SLM process, ensuring compliance with the latest technological advancements.

Scope of Application:

• Metal-ceramic crowns and bridges
• Partial denture prosthetics
• Implant-supported prosthetics
• Orthodontic appliances

Technical Specifications:

• Product Name: Mediloy® S-Co
• Type: Cobalt-Chromium Powder for SLM Procedure
• Content: 5 kg bottle
• Composition: Co 63.9%, Cr 24.7%, W 5.4%, Mo 5.0%, Si 1.0%
• Base Metal: Cobalt
• Solidus Temperature: 1380°C
• Liquidus Temperature: 1420°C
• Vickers Hardness: 470 HV10
• Yield Strength: 1090 MPa
• Elongation at Break: 4%
• Density: 8.6 g/cm³
• Elastic Modulus: 215 GPa
• Tensile Strength: 1315 MPa
• ISO Type: ISO 22674 Type 5
• Coefficient of Thermal Expansion (CTE): 14.3 (10ˉ⁶ Kˉ¹)

With Mediloy® S-Co, dental technicians gain access to an alloy that offers unparalleled mechanical properties, safety, and ease of use. Its superior strength, biocompatibility, and corrosion resistance make it the perfect choice for producing high-quality crowns, bridges, partial dentures, and implant prosthetics with consistency and precision.